Episode 37 – What do I do if my glaze is hard panning?

On today’s episode of For Flux Sake our hosts talk about dipping glazes and what to do when your glaze hard pans at the bottom of the bucket. Listen to episode 37 now on your favorite podcast app or stream here.

Kathy, Matt, and Rose are excited to announce that the first in-person taping of For Flux Sake will be happening at this year’s NCECA in Cincinnati. If you come to the podcast room at 1pm on Friday March 17th you can join the live taping and have your questions answered. It’s going to be a blast so bring your questions and your friends!

If you have a ceramic chemistry problem you’d like help with, send us a voice memo with your question to forfluxsakepodcast@gmail.com. To see the supplemental info, we talked about in this episode, visit the blog at www.ceramicmaterialsworkshop.com/cmw-blog.

Share this Episode

Explore our courses!

Not sure where to start? Get help finding your learning path.

Start Learning

Recent Podcast Episodes

Today your favorite glaze experts answer a listener's question about judging the melt of an ash glaze, methods for wet mixing bentonite, and whether or not it's safe to use industrial dinnerware made before lead was regulated. They also open the show talking about why you should never crush encapsulated stains.
Have you ever wondered what makes a bronze glaze work? This week on the show the gang answer a listener's question about metallic oxides in glazes, and discuss the finer points of what makes a pinhole a pinhole.
Have you noticed how a tight kiln pack can slightly change your cones? In this week’s episode the gang talk about why this happens, as well as answer a listener's question about firing a balloon inside of a ceramic sculpture.